PP Barium Sulfate Masterbatch (TC2000)

Delivery term:The date of payment from buyers deliver within days

Price:
Negotiable
minimum:
Total supply:
Delivery term:
The date of payment from buyers deliver within days
seat:
Beijing
Validity to:
Long-term effective
Last update:
2017-12-26 18:02
Browse the number:
385

Send an inquiries

Company Profile

Suzhou Haixiang Plastic Chemical Co.,Ltd: Contact:
haixiang(Mr.); Email:; Telephone:; Area:
Beijing; Address:
Yuanzhong Bridge West, Guangfu Town Industrial Zone, Wuzhong District, Suzhou, Jiangsu, China; Website: http://www.sz-flameretardant.com/ http://haixiang.mingzhuqizhong.com/

Product details

Introduction

PP barium sulfate masterbatch PP-TC2000 using pp resins as carrier, With 2500 mesh of precipitated barium sulfate by high speed mixing, dispersion, coupling, and then the brace twin-screw extruder pelletizing.Chooses barium sulfate high purity, good whiteness, does not affect the product of the flame retardant effect, and have a good reinforcing and increasing rigidity.Barium sulfate containing 70%, good dispersibility, high liquidity.

Application

Mainly used in PP Injection molding, blown film, sheet etc.

Index

Appearance	White Granular
Density g/cm3	1.34
Solubility Index g/min,200℃5kg	5.0
Water Content %≤	0.05
Melting Temp ℃≥	180
Decomposition Temp℃≥	330

Recommended ratio

PP raw material : Flame masterbatch (ZRPP+) :Filler masterbatch(PP-TC2000)=40:30:30

Technical Data

Properties	Test Methods	Unit	Test Value
Density	ASTM D-792	g/cm3	1.3
Melt Index 200℃/5KG	ASTM D-955	g/10min	5
Tensile Strength	ASTM- D638	MPa	23.6
Elongation At Break	ASTM-D638	%	68
Flexural Strength	ASTM-D790	MPa	35
Flexural Modulus	ASTM-D790	MPa	2050
Izod Impact Strength Notched	ASTM-D256	KJ/m2	7.5
Flame Retardancy 3.2mm	UL94	--	V0
Color			Nature Color